F605-Epoxy Primer
Release time：2016-07-11 17:19:15 Click volume：
Product Name/Model：F605-Epoxy Primer
Characteristic: Good fillibility, easy sanding, give excellent rust proofing for bare metal, good adhesion power to steel, aluminium, galvanized steel and stainless steel, excellent chemical corrosion resistance and rust resistance.
Substrates
|
Dried and sanded existing finishes, steel, aluminium, stainless steel, galvanized steel, glass fiber reinforced plastic.
|
Surface Cleaning
|
Wash by warm soap, remove wax, silicon and other contaminations with degreaser, sandingwith P800-P1000, wash with clean water then keep dry; again with degreaser.
|
Mixing Ratio
|
F605 Epoxy Primer
|
MSH105 Epoxy Hardener
|
MSD-63Epoxy Thinner
|
|
4
|
1
|
1~2
|
＜30℃
|
F605 Epoxy Primer
|
MSH105 Epoxy Hardener
|
MSD-63 Epoxy Thinner
|
Spray Viscosity
|
16-19s to drop off, in 4# viscosity cupat 25°C,
|
Pot-life
|
At 20°C, 3 hours with hardener.
|
ReTreatment
|
Sanded with P600 or P800 sand paper, do following construction after drying
|
Spray Gun Set Up
|
Gravity Feed: 1.2-1.5mm 4-5kg/cm 2；Suction Feed: 1.4-1.6mm 4-5kg/cm 2
|
Spray Technology
|
Coats&Thickness: 2-3 coats, total 25-35um.Flash-Off Time: At 25°C, 5-10minutes between two coats, it depends on temperature and paint film.
|
Drying Time
|
A. Allow 10-20 minutes air-drying,then 60°C baking 30 minutes, can sand after cool down. B. Air-drying time 3 hours, at 20°C.
|
Shelf Life
|
2 years in original sealed can, cool and dry place at 25℃.
|
Package
|
1L×12 or 3.75L×4
|
Note:
1. The substrate must be cleaned and sanded before spray, wet sanding P800-1000 and then dry.
2. At ambient temperature higher than 30℃, add appropriate Retarder Solvent into thinner to avoid blushing. For more details, please refer to technical data sheet of Retarder Solvent.
3. The products mixed with hardener should be used up soon and can not be restore for future use; clean equipments immediately with thinner after application, otherwise it is very difficult to be cleaned after dry.